HIGH QUALITY BEST PRICE CEM III 32,5 R BLAST FURNACE SLAG CEMENT

Granulated blast furnace slag powder technical indicators

 

Inspection items

Level

S105

S95

S75

density of the:g/cm3       Not less than

2.80

Specific surface area:m2/kg Not less than

500

400

300

Active index:%

Not less than

7day

95

75

55

28 day

105

95

75

Fluidity than:%         Not less than

95

Water content:%         Not less than

1.0

Sulphur trioxide:%      Not less than

4.0

Chloride ion:%         Not less than

0.06

Loss on ignition:%       Not less than

3.0

Note:Higher level of slag powder can be produced according to customer requirements

Packing:1.Bulk;2.50kg Bag;3.1000kg Bag

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Granulated blast furnace slag powder chemical composition : (%)

Chemical Constituents

SiO2

CaO

MgO

Al2O3

MnO

TiO2

Fe2O3

40

About

45

About

8.0

About

12.0 About

0.2 About

0.4 About

0.3 About

 

 

If you have any requirements,you  can feel free to contact with me.

HIGH QUALITY BEST PRICE CEM III 32,5 R BLAST FURNACE SLAG CEMENT

  • ASTM C150/C150M-22
    Standard Specification For Portland Cement
    1.1This specification covers ten types of portland cement, as follows (see Note 2):

    1.1.1Type I - For general use, when the special properties specified for any other type are not required.

    1.1.2Type IA - Air-entraining cement for the same uses as Type I, where air-entrainment is desired.

    1.1.3Type II - For general use, more especially when moderate sulfate resistance is desired.

    1.1.4Type IIA - Air-entraining cement for the same uses as Type II, where air-entrainment is desired.

    1.1.5Type II(MH) - For general use, more especially when moderate heat of hydration and moderate sulfate resistance are desired.

    1.1.6Type II(MH)A - Air-entraining cement for the same uses as Type II(MH), where air-entrainment is desired.

    1.1.7Type III - For use when high early strength is desired.

    1.1.8Type IIIA - Air-entraining cement for the same use as Type III, where air-entrainment is desired.

    1.1.9Type IV - For use when a low heat of hydration is desired.

    1.1.10Type V - For use when high sulfate resistance is desired.